Product name
|
Viscosity
|
Solid content
|
Solvent
|
100% modulus
|
Tensile Strength
|
Elongation(%)
|
Characteristic
|
Use
|
|
4010HV
|
110～140
|
50±1
|
TOL/MEK
|
2.5
|
35.0
|
520
|
Excellent hydrolysis resistance, good initial tack, good adhesion to PVC/ABS and other plastics
|
Shoe leather, suede, electrostatic flocking
|
|
4030HV
|
40～70
|
50±1
|
DMF/TOL/M-MEK
|
1.0
|
15.0
|
800
|
Good hydrolysis resistance, good hand feeling, softness, good adhesion, low cost
|
Two suede, luggage leather, coating
|
|
4070K
|
70～110
|
64±1
|
TOL/MEK
|
2.5
|
31.0
|
510
|
Dry paste, excellent hydrolysis resistance, good initial tack
|
Garment leather, electrostatic flocking
|
|
4050HV
|
40～70
|
50±1
|
DMF/TOL
|
4.5
|
35.0
|
800
|
Good hydrolysis resistance, good hand feeling, soft, economical and good adhesion
|
Two-layer leather, luggage leather
|
|
4090HV
|
40～70
|
65±1
|
DMF/TOL/MEK
|
1.0
|
15.0
|
500
|
Good hydrolysis resistance, good hand feeling, soft, economical and good adhesion
|
Shoe leather, two suede
|
|
TA-265DM
|
75～125
|
65±1
|
DMF/MEK
|
2.5
|
34.0
|
520
|
Excellent hydrolysis resistance, excellent low temperature resistance, good initial tack, excellent NOx resistance
|
Shoe leather, microfiber leather
|
|
BZ-280F
|
25～45
|
80±1
|
MEK/TOL
|
2.5
|
34.0
|
80
|
High solid content, excellent hydrolysis resistance, excellent low temperature resistance and flexibility, good adhesion, dry foaming resin
|
Shoe leather, microfiber leather
|
|
BZ-1
|
120～200
|
65±1
|
TOL/MEK
|
1.5
|
7.0
|
500
|
Good hydrolysis resistance, good hand feeling, soft, economical and good adhesion
|
Shoe leather, suede, composite cloth
|
|
TA-265DM
|
75～125
|
65±1
|
DMF/MEK
|
2.5
|
34.0
|
520
|
Excellent hydrolysis resistance, excellent low temperature resistance, good initial tack, excellent NOx resistance
|
Shoe leather, microfiber leather
|